Ultramid B3EG3 is a 15% glass fiber reinforced injection molding PA6 grade.

Ultramid B3EG6 is a 30% glass fiber reinforced injection molding PA6 grade.

Ultramid B3EG7 is a 35% glass fiber reinforced injection molding PA6 grade.

Ultramid B3K is an easy flowing, stabilized PA6 product for fast processing.

Ultramid B3S Easy flowing, finely crystalline injection moulding grade for very fast processing.

Ultramid B3WG5 is a 25% glass fiber reinforced injection molding PA6 grade with heat aging resistance.

Ultramid B3WG6 is a 30% glass fiber reinforced, heat stabilized injection molding PA6 grade.

Ultramid B3Z is an impact-modified, pigmented black, unreinforced PA6 for injection molding.

Ultramid B3ZG3 is an impact-modified, 15% glass fiber reinforced injection molding PA6 grade.

Ultramid B3ZG6 is an impact-modified, 30% glass fiber reinforced injection molding PA6 grade.

Ultramid B3M6 is a 30% mineral reinforced injection molding PA6 grade.

Ultramid A3EG3 is a 15% glass fiber reinforced injection molding PA66 grade.

Ultramid A3EG6 is a 30% glass fiber reinforced injection molding PA66 grade.

Ultramid A3EG7 is a 35% glass fiber reinforced injection molding PA66 grade.

Ultramid A3HG2 is a 10% glass fiber reinforced injection molding PA66 grade.

Ultramid A3HG5 is a 25% glass fiber reinforced injection molding PA66 grade.

Ultramid A3HG7 is a 35% glass fiber reinforced injection molding PA66 grade.

Ultramid A3K is an easy flowing, pigmented black, injection molding grade PA66.

Ultramid A3W Easy flowing, heat aging resistant injection moulding grade for fast processing.

Ultramid A3WG6 is a 30% glass fiber reinforced and heat resistance injection molding PA66 grade.

Ultramid A3WG7 is a 35% glass fiber reinforced and heat resistance injection molding PA66 grade.

Ultramid A3X2G5 Glass fibre reinforced injection moulding grade with improved flame retardance

Ultramid A3Z Impact-modified and stabilized injection moulding grade for components

Ultramid A4H High heat aging resistant, medium viscosity injection moulding grade

PA6 B27E--尼龍主要缺點

注塑技術(shù)要求較嚴：微量水分的存在都會對成型質(zhì)量造成很大損害;因熱膨脹作用使制品尺寸穩(wěn)定性較難控制；制品中尖角的存在會導(dǎo)致應(yīng)力集中而降低機械強度；壁厚如果不均勻會導(dǎo)致制件的扭曲、變形；制件后加工時設(shè)備精度要求高。會吸收水、醇而溶脹，不耐強酸及氧化劑，不能作耐酸材料使用。耐光性較差。在長期偏高溫環(huán)境下會與空氣中的氧發(fā)生氧化作用,開始時顏色變褐，繼面破碎開裂。易吸水。吸水性大，飽和水可以達到3%以上.一定的程度上影響尺寸穩(wěn)定性和電性能，特別是薄壁件增厚影響較大；吸水亦會大大降低塑料的機械強度。在選材時，應(yīng)顧及使用環(huán)境及與別的元件的配合精度的影響。纖維增強可降低樹脂吸水率，使其能在高溫、高濕下工作。尼龍與玻璃纖維親合性十分良好。常用于制作梳子、牙刷、衣鉤、扇骨、網(wǎng)袋繩、水果外包裝袋等等。性，但不可長期與酸堿接觸。值得注意的是,加入玻纖后,尼龍的抗拉強度可提高2 倍左右,耐溫能力也相應(yīng)得到提高。

PA6 B27E--PA6為乳白色或微黃色透明到不透明角質(zhì)狀結(jié)晶性聚合物，可自由著色，韌性、耐磨性、自潤滑性好、剛性小、耐低溫，耐、能慢燃，離火慢熄，有滴落、起泡現(xiàn)象，成型加工性：可注塑、吹塑、澆塑、噴涂、粉末成型、機加工、焊接、粘接。PA6是吸水率的PA，尺寸穩(wěn)定性差，并影響電性能（擊穿電壓）。PA6使用溫度可達180℃,加抗沖改性劑后會降至160℃用15%-50%玻纖增強，可提高至199℃，無機填充PA能提高其熱變形溫度。

PA6 B27E--PA6優(yōu)點：優(yōu)異的電氣性能、軟化點高、表面光滑比較耐磨、耐疲勞、PA6抗拉強度比較接近屈服強度，而比ABS高一倍多。而且對于尼龍PA6沖擊應(yīng)力振動單位吸收能力較強，并且比縮醛樹脂更好。容易成型、易染色、迅速成型、生產(chǎn)效率高等。